Enhance Adhesion Between The Paint Film and The Plastic Substrate 1K Transparent Plastic Primer

• Customization: Available
• CAS No.: 2010900835
• Formula: Car Clear Coat Hardener
• Model NO.: . 1K Transparent Plastic Primer
• Color: Green
• Appearance: Liquid
• Main Raw Material: Acrylic
• Paint Film Property: Antiseptic Paint
• Method: Spray
• Level: Finish Coat
• Certification: ISO14001, ISO9001
• Substrate: Steel
• Components: Film Forming Matter
• Formation Mechanism: Conversion Type
• Characteristic: Fast Drying One Pack Primer Surfacer
• Suitable to: Cover Minor Defects in Surface of Putty or Existi
• Easy to Apply with: Strong Filling Power and Ease
• Surstrates Treatment: Remove Wax, Grease or Other Contaminations with De
• Mixing Ratio: 1:1
• Pot Life: 48 Hours@20
• Composition: Modulation From. Synthesis of Fatty Ester Resin, a
• Usage: Spraying After Use Our Factory Nitro Lacquer Thin
• Not Suitable for: Direct Application Over Bare Meta
• It Is Recommended for: Spot Repair But Not for Large Area Application
• Colours: Transparent
• Transport Package: Carton
• Specification: 1Lx12cans/carton
• Trademark: rapicoat
• Origin: Guangzhou, China
• HS Code: 32018090
• Production Capacity: 464346

Product Description

We main manufacture automotive paint included
a) 2K topcoat in different solid colors
b) 1K basecoat  in different solid colors, metallic colors ,silver and pearl colors  
c)  2K standard / high solid clear coat ,hardener, thinner to make the surface more shiny:
d)  1k ,2k primer surface can be white,gray colour
e) 2K primer surfacer: the intermediate layer
f) epoxy primer/alloy primer:  the bottom layer
g) plastic primer                        
can be tailor customer brand easily With superior good quality and competitive prices less 5% profits,
we are looking for local overseas distributors
Any interested enquiries are welcome to contact us.

RAP-20  1K Transparent Plastic Primer
Characteristic:	Characteristic: Volatile dry plastic primer, used to enhance adhesion between the paint film and the plastic substrate.
Substrates	Plastic substrates such as PP,PA,PVC
Substrates Treatment	use the degreaser to clean the substrate
Mixing ratio	Do not need to mix with other products, use directly
Pot Life	Volatile products, use immediately
Spraying viscosity	11±2S@25ºC
No. of Coats	2 Coats
Drying time Time	10-20 Minutes @20ºC
Each Thickness	About 5-10 Micron
Spray pressure	Gravity feed   1.2-1.5 Suction feed,   1.2-1.7,Spray pressure 3-4kg/cm²
Sandability and Polishabiility	on need to sand
Shelf Life	5 years in original sealed(can continue to use after passing inspection )
Packaging	1LX12tins/ctn

1K Primer surfacer
Fast dry,easy sanding,one pack primer surfacer,easy to use,strong filling power,excellent coverage, good adhesion between layers, suitable to cover minor defects of the paint film.
Substrate	The dried and be polished old paint surface, or completely polished putty surface.
Not suitable Substrate	Aluminum, stainless steel, plastic, galvanized steel and timber
Surface Cleaning	Remove wax,silicon, and other contaminations with degreaser
Mixing Ratio	RAP 1K Primer Surfacer : Standard thinner=1: 0.8~1.0
(1: 0.8~1.0)
No.of Coats	2-3 coats,total 15--25um
Interval time	5-10 minutes, 25ºC
Spray gun and pressure	Gravity gun. (up pot)  1.4-1.6mm    3-5 kg/CM2
	Siphon gun (down pot)  1.7-1.8mm    3-5 kg/CM2
Drying time	30 minutes, 25ºC
Sanding	Dry sanding with 400#---600# sandpaper or wet sanding with 800#----1000# sandpaper
Re-coat	Could be re-coat all colors paint and plasticintermediate paint after dry and sanding.
Shelf life	Above 2 years in original sealed can in cool and dry place at 20ºC
colours	Grey in common,also have lightergrey, red,medium yellow,blue,green,black,white and egg yellow
Packing	4kg can
Note:
Not suitable for direct application over bare metals like the aluminum, stainless steel, plastic,  galvanized steel & wood surface.
It is recommmended for small part repair but not for large area application.
It is recommended to use 2K primer surfacer to achieve good adhesion and strong corrosion resistance.